PA66(尼龙66)22G5/长春化工(漳州)/物性表参数
以下是PA66(尼龙66)22G5/长春化工(漳州)/物性表参数
| 密度 | 1.35 g/cc | 0.0488 lb/in³ | |
| 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | |
| 吸水率 |
3.4 %
@Thickness 2.00 mm
|
3.4 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 水分吸收 |
0.900 %
@Thickness 2.00 mm
|
0.900 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 粘度 |
85370 cP
@Shear Rate 5000 1/s, Temperature 280 °C
|
85370 cP
@Shear Rate 5000 1/s, Temperature 536 °F
|
ISO 11403-1 -2 |
|
138900 cP
@Shear Rate 5000 1/s, Temperature 270 °C
|
138900 cP
@Shear Rate 5000 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
|
243400 cP
@Shear Rate 5000 1/s, Temperature 260 °C
|
243400 cP
@Shear Rate 5000 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
|
270750 cP
@Shear Rate 500 1/s, Temperature 280 °C
|
270750 cP
@Shear Rate 500 1/s, Temperature 536 °F
|
ISO 11403-1 -2 | |
|
441600 cP
@Shear Rate 500 1/s, Temperature 270 °C
|
441600 cP
@Shear Rate 500 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
|
774800 cP
@Shear Rate 500 1/s, Temperature 260 °C
|
774800 cP
@Shear Rate 500 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
| 粘度测试 | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
| 125 MPa | 18100 psi | DAM; ISO 527-1/-2 | |
| 抗张强度 |
8.79 MPa
@Strain 0.230 %, Temperature 150 °C
|
1270 psi
@Strain 0.230 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 |
|
12.0 MPa
@Strain 0.240 %, Temperature 90.0 °C
|
1740 psi
@Strain 0.240 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
15.95 MPa
@Strain 0.470 %, Temperature 150 °C
|
2313 psi
@Strain 0.470 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
22.76 MPa
@Strain 0.480 %, Temperature 90.0 °C
|
3301 psi
@Strain 0.480 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
24.06 MPa
@Strain 0.700 %, Temperature 150 °C
|
3490 psi
@Strain 0.700 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
25.92 MPa
@Strain 0.400 %, Temperature 40.0 °C
|
3759 psi
@Strain 0.400 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
31.12 MPa
@Strain 1.10 %, Temperature 150 °C
|
4514 psi
@Strain 1.10 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
34.25 MPa
@Strain 0.790 %, Temperature 90.0 °C
|
4968 psi
@Strain 0.790 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
37.13 MPa
@Strain 0.540 %, Temperature 40.0 °C
|
5385 psi
@Strain 0.540 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
41.37 MPa
@Strain 0.570 %, Temperature 23.0 °C
|
6000 psi
@Strain 0.570 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
41.5 MPa
@Strain 0.470 %, Temperature 23.0 °C
|
6020 psi
@Strain 0.470 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
42.25 MPa
@Strain 1.55 %, Temperature 150 °C
|
6128 psi
@Strain 1.55 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
44.11 MPa
@Strain 2.01 %, Temperature 150 °C
|
6398 psi
@Strain 2.01 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
44.88 MPa
@Strain 1.15 %, Temperature 90.0 °C
|
6509 psi
@Strain 1.15 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
52.61 MPa
@Strain 3.26 %, Temperature 150 °C
|
7630 psi
@Strain 3.26 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
54.28 MPa
@Strain 0.980 %, Temperature 40.0 °C
|
7873 psi
@Strain 0.980 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
55.02 MPa
@Strain 2.75 %, Temperature 150 °C
|
7980 psi
@Strain 2.75 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
57.51 MPa
@Strain 1.63 %, Temperature 90.0 °C
|
8341 psi
@Strain 1.63 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
63.12 MPa
@Strain 2.08 %, Temperature 90.0 °C
|
9155 psi
@Strain 2.08 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
63.72 MPa
@Strain 0.650 %, Temperature -20.0 °C
|
9242 psi
@Strain 0.650 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
67.98 MPa
@Strain 0.820 %, Temperature 0.000 °C
|
9860 psi
@Strain 0.820 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
71.93 MPa
@Strain 3.50 %, Temperature 90.0 °C
|
10430 psi
@Strain 3.50 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
72.3 MPa
@Strain 0.770 %, Temperature 0.000 °C
|
10500 psi
@Strain 0.770 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
|
73.4 MPa
@Strain 1.26 %, Temperature 40.0 °C
|
10600 psi
@Strain 1.26 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
73.91 MPa
@Strain 1.18 %, Temperature 23.0 °C
|
10720 psi
@Strain 1.18 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
74.49 MPa
@Strain 2.80 %, Temperature 90.0 °C
|
10800 psi
@Strain 2.80 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
78.89 MPa
@Strain 0.830 %, Temperature -20.0 °C
|
11440 psi
@Strain 0.830 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
|
79.11 MPa
@Strain 1.75 %, Temperature 40.0 °C
|
11470 psi
@Strain 1.75 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
84.04 MPa
@Strain 1.04 %, Temperature 23.0 °C
|
12190 psi
@Strain 1.04 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
94.42 MPa
@Strain 2.82 %, Temperature 40.0 °C
|
13690 psi
@Strain 2.82 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.33 MPa
@Strain 1.96 %, Temperature 23.0 °C
|
14552 psi
@Strain 1.96 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.68 MPa
@Strain 1.34 %, Temperature 0.000 °C
|
14602 psi
@Strain 1.34 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.92 MPa
@Strain 2.18 %, Temperature 40.0 °C
|
14637 psi
@Strain 2.18 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
101.62 MPa
@Strain 1.11 %, Temperature -20.0 °C
|
14739 psi
@Strain 1.11 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
118.66 MPa
@Strain 1.78 %, Temperature 23.0 °C
|
17210 psi
@Strain 1.78 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
120.54 MPa
@Strain 1.46 %, Temperature 0.000 °C
|
17483 psi
@Strain 1.46 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
|
127.28 MPa
@Strain 1.98 %, Temperature 0.000 °C
|
18460 psi
@Strain 1.98 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
134.63 MPa
@Strain 1.66 %, Temperature -20.0 °C
|
19526 psi
@Strain 1.66 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
142.85 MPa
@Strain 1.74 %, Temperature -20.0 °C
|
20719 psi
@Strain 1.74 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
|
157.09 MPa
@Strain 2.33 %, Temperature 0.000 °C
|
22784 psi
@Strain 2.33 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 伸长率 (断裂) | 2.0 % | 2.0 % | DAM; ISO 527-1/-2 |
| 2.6 % | 2.6 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | DAM; ISO 527-1/-2 | |
|
3.213 GPa
@Temperature 150 °C
|
466.0 ksi
@Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
3.595 GPa
@Temperature 150 °C
|
521.4 ksi
@Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
5.515 GPa
@Temperature 60.0 °C
|
799.9 ksi
@Temperature 140 °F
|
50%RH; ISO 11403-1 -2 | |
|
5.62 GPa
@Temperature 60.0 °C
|
815 ksi
@Temperature 140 °F
|
DAM; ISO 11403-1 -2 | |
|
10.386 GPa
@Temperature -20.0 °C
|
1506.4 ksi
@Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
10.498 GPa
@Temperature -20.0 °C
|
1522.6 ksi
@Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 割线模量 |
4.16 GPa
@Strain 2.06 %, Temperature 40.0 °C
|
603 ksi
@Strain 2.06 %, Temperature 104 °F
|
 |
PA66(尼龙66)22G5/长春化工(漳州)/物性表参数 |
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：12258 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：10810 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：10507 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：8845 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：7778 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：7752 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：7245 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：6722 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：6403 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：6354 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：6339 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：6252 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：6057 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5980 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：5930
推荐文章
-
TPU(热塑性聚氨酯弹性体)2792A/科思创/物性表参数
科思创(Covestro)的Desmopan(德士模班)TPU 2792A是全球品级的热塑性聚氨酯弹性体，密度是(ISO1183-1)1205 kg/m ，性能是冷挠曲性, 抗磨损, 耐化学性, 耐磨, 防刮, 抗撕裂。 以下是TPU(热塑性聚氨酯弹
-
PPA(聚邻苯二甲酰胺)EX00548C/沙伯基础/物性表参数
SABIC(沙伯基础)LNP/THERMOCOMP/Compound/ PPA EX00548C 是一种基于聚醚酰亚胺树脂含有专有填料的化合物，这种材料的附加特性包括:清洁复合系统，耐磨。 以下是SABIC(沙伯基础)LNP/THERMOCOMP/Compoun
-
PPS(聚苯硫醚)H501|TORAY(东丽)物性表参数
东丽TORELINA树脂 PPS H501 是一种加MD60增强, 导电, 高热传导级别的PPS塑胶原材料,东丽均有交联和线型两种类PPS, 从基材的聚合到复合工程均有自己的生产线, 为客户提供多种多样的产品规格
-
TPE(热塑性弹性体)TF7PEN/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG热塑宝K TPE TF7PEN 是一款自然色, 硬度67A,用于食品接触应用的材料解决方案，能提供卓越的 LDPE、LLPPE 和 HDPE 的包胶性能,该系列有自然色和半透明颜色可供选择,典型应用
-
TPE(热塑性弹性体)TM3ADT/凯柏胶宝/物性表参数
凯柏胶宝KRAIBURG热塑宝K TPE TM3ADT 是一款医疗级TPE,硬度是34A半透明TPE材料,MC/AD1系列是用于基本医疗批复（如 ISO 10993-5）应用的材料解决方案。该系列的特点为对PC、ABS和PC/ABS等极性热塑性
-
PA66(尼龙66)CM3216G35UB1|TORAY(东丽)物性表参数
TORAY(东丽)Nylon树脂AMILAN PA66 CM3216G35UB1 是一种加35%玻纤增强，耐氯化钙，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是195MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客
-
PA6(尼龙6)B3U|BASF(巴斯夫)物性表参数
巴斯夫ULTRAMID PA6 B3U 是一种注塑级、阻燃、无卤素和和UL94V0标准原料，技术成型零件用于电气工程，BASF尼龙是以聚酰胺为基础的聚酰胺成型化合物，由于它们良好的性质 ，这些材料
-
SURLYN(沙林树脂)9320|陶氏杜邦|物性表参数
陶氏杜邦 SURLYN 9320 是一种沙林 塑料树脂 ，也是一种乙烯酸共聚物的离聚物，这种聚合物材料可以在传统的挤出和注塑设备中加工，这些设备设计用于加工聚乙烯和乙烯共聚物型树脂，
-
TPE/K TC8FLN/TPE物性参数
德国胶宝Kraiburg THERMOLAST TPE K TC8FLN 物性参数 K TC8FLN是德国胶宝公司Kraiburg THERMOLAST塑性弹性体TPE型号之一 德国胶宝Kraiburg THERMOLAST TPE K TC8FLN 物性参数 以下是德国胶宝Kraiburg THERMOLAST TPE
-
PA66(尼龙66)A3ZG5|BASF(巴斯夫)物性表参数
巴斯夫ULTRAMID PA66 A3ZG5 是一种冲击改性，加玻璃纤维25%增强注射成型等级，具有良好的尺寸稳定性，巴斯夫尼龙是以聚酰胺为基础的聚酰胺成型化合物，由于它们良好的性质 ，这些