VALOX(沙伯基础)815/PBT热塑性聚酯/物性表参数
沙伯基础创新塑料SABIC的VALOX 815 PBT是一种加15% GR PBT+ PET，表面光洁度好,典型的应用是热风枪外壳组件、工业胶枪、电器外壳和把手。
 |
沙伯基础创新塑料的VALOX 815 PBT物性表参数PDF文档下载 |
以下是VALOX(沙伯基础)815/PBT热塑性聚酯/物性表参数
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 100 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 100 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 6200 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 155 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 155 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5000 | MPa | ASTM D 790 | |
| Hardness, Rockwell R | 120 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 17 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 100 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 6200 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 145 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 4 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 5200 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 102 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 30 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 30 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 390 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 390 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 6 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -20°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 204 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 160 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.5E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 9.32E-05 | 1/°C | ASTM E 831 | |
| CTE, 60°C to 138°C, flow | 5.4E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 3.23E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 5.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.41E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.76E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 204 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 167 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 125 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.43 | - | ASTM D 792 | |
| Specific Volume | 0.7 | cm³/g | ASTM D 792 | |
| Water Absorption, 24 hours | 0.06 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.4-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 1.5-3.2 mm | 0.4-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2-4.6 mm | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.6-1 | % | SABIC method | |
| Mold Shrinkage, xflow, 1.5-3.2 mm | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage, xflow, 3.2-4.6 mm | 0.8-1.1 | % | SABIC method | |
| Melt Flow Rate, 250°C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 60 | g/10 min | ASTM D 1238 | |
| Density | 1.43 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 12 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 50 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 155 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | 5.6E+16 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 3.2 mm | 22 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23.6 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 100 Hz | 3.6 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 3.5 | - | ASTM D 150 | |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 2 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.6 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 175 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 4-6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260-285 | °C | ||
| Nozzle Temperature | 265-275 | °C | ||
| Front - Zone 3 Temperature | 260-280 | °C | ||
| Middle - Zone 2 Temperature | 255-280 | °C | ||
| Rear - Zone 1 Temperature | 240-260 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 60-110 | °C |
温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.
热门文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表参数台化TAIRILOY PC/ABS AC3100是无氯、无溴、无锑阻燃级合金树脂，应用于笔记型电脑外壳、光碟机Loader及 Tray盘、萤幕外壳、数位相机外壳、事务机器外壳、家用电器外壳、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性
浏览量：12190 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表参数台化TAIRILOY PC/ABS AC2300是电镀级合金树脂，应用于汽车门把、仪表板、轮圈盖、汽车零件、消费性电子元件，TAIRILOY PC/ABS合胶具有ABS的加工性及耐低温机械性能，亦同时具有PC的高冲击性及耐热性特质，可应用於汽车零件、3C电子產品外壳、消费性电子元件、家电外壳、玩具、板材等產品上，其应用端多元化，本厂设有
浏览量：10742 -
TRITAN(美国伊士曼)TX1001/PCTG(共聚聚酯)物···美国伊士曼TRITAN PCTG TX1001 是一种无定形共聚酯，具有极好的外观和清晰度,EastmanTritanTX1001包含一个基于脱模来源于蔬菜来源。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化
浏览量：10449 -
ABS塑料树脂/PA-757/奇美实业/物性表参数奇美实业POLYLAC ABS PA-757 是一般级高光泽性、超高刚性、特佳弯曲强度的ABS树脂,熔融指数是22.g/10min,用途是电视机前壳、复印机外壳 、电话机壳 、化妆品盒 、轮胎盖,奇美的POLYLACABS树脂
浏览量：8802 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是转换成双轴取向的薄膜，使用温度高达300°F(150°C)，该薄膜具有优良的光学性能、良好的可加工性和优良的扭折性，这些特性使4032D薄膜成为层压和其他包装应用的理想产品，其他性能包括阻隔风味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表参数PDF文档下载以下是PLA(聚乳酸)4032
浏览量：7754 -
PC(聚碳酸酯)FR6005/科思创(Makrolon)物性表···科思创(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品级; 体积熔融指数MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐冲击，阻燃等级，透明高光泽，适用于电子/电气产品。 以下是PC(聚碳酸
浏览量：7722 -
PA66(尼龙66)CM3006G-30|TORAY(东丽)物性表···TORAY(东丽)Nylon树脂AMILAN PA66 CM3006G-30 是一种加30%玻纤增强，耐热级别的尼龙66原料，拉伸强度在23℃测试条件是190MPa,更是一种含有酰胺基(-CONH-)的热塑性工程塑料，此外还为客户的各种需
浏览量：7229 -
POM(聚甲醛树脂)M90-44/宝理塑料/物性表参数···宝理塑料(夺钢)DURACON POM M90-44是一种标准全球品级型号,高流动性聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-ray 光盘播放器等AV机器；打印机、复印机等OA机器；洗衣机、冰箱、剃须刀等家用电器；油箱盖、燃料油泵、安全带零部件以及汽车内饰用品等
浏览量：6696 -
Bayblend(拜本兰)FR3010|科思创(PC/ABS合金···科思创Bayblend PC/ABS FR3010 是加阻燃,剂维卡软化点温度/ B 120 = 110C;耐热性增加;UL认可94 V-0为1.5 mm;灼热丝温度(GWFI):在2.0毫米960C;改进的化学抗性和应力开裂行为;继任者FR2010. PC/ABS是聚碳酸
浏览量：6372 -
PP(聚丙烯)HJ730|韩华道达尔(Hanwha)物性表···韩华道达尔(Hanwha)高抗冲PP HJ730是与普通均聚PP相比具有高等规高结晶度的特点，这一产品的结晶性能使其具有更好的强度和耐热性。HJ730非常有助于在电子电器产品和高强度汽车部件上使用，这些部件需要在高温环境下长期暴露.其特点是：高强度、超高耐热、高结晶度、良好的表面硬度、良好的色粉分散性。韩华道达尔PP HJ730物
浏览量：6322 -
PA12(尼龙12)TR90|瑞士EMS化学|物性表参数科思德塑胶网站提供瑞士EMS化学PA12 TR90的物性表参数下载，并且有Grilamid PA12 TR90塑胶粒销售，为您提供详细的瑞士EMS化学PA12(尼龙12)TR90资料以及报价。
浏览量：6319 -
Makrolon(模克隆)2407(科思创)PC(聚碳酸酯)···科思创Makrolon 2407 PC材料介绍： Makrolon 2407 PC是全球品级; 体积熔融指数19 厘米 3 /10分钟; 普通用途; 紫外线稳定; 易脱模; 注塑成型; 可提供透明, 半透明和不透明颜色. Makrolon 2407物性表P
浏览量：6230 -
TRITAN(美国伊士曼)TX1501HF/PCTG(共聚聚酯···美国伊士曼TRITAN PCTG TX1501HF 是一种伊士曼TRITAN的高流动级材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相对于伊士曼TRITAN共聚酯TX1001，其他突出的特点包括良好的韧性，水解稳定性，耐热性
浏览量：6040 -
PC/ABS(PC+ABS合金)PC-540|奇美实业|物性表···奇美实业WONDERLOY PC/ABS PC-540是防火级不含卤素的难燃PC合金树脂,熔融指数是22.g/10min,用途是机顶盒、投影机、显示器前框、3C数码产品、变压器、电视游乐器、小平板计算机、网通产品,为了增加PC在薄肉产品的耐冲击性，可加入ABS树脂进行掺合(blending)，可形成同时具有高刚性及高耐冲击性之新材料,一般用于计算机外壳及
浏览量：5944 -
PC(聚碳酸酯)L-1250Y|嘉兴帝人|物性表参数嘉兴帝人Panlite PC L-1250Y 是一款熔融体积流量是8MVR，特性是 脱模性能良好, 中等粘性 ，通用级应用，在Japan实现工业化生产的聚碳酸酯树脂，长期以来，帝人一直致力于其性能的提高和
浏览量：5906
推荐文章
-
PP(聚丙烯)PP7935E1/埃克森美孚(ExxonMobil)物性表参数
埃克森美孚(ExxonMobil)PP PP7935E1是一种具有高结晶度、低抗冲击强度的共聚物树脂，熔体流动速率(230°C/2.16kg)是100克/10分钟，密度(23°C)是0.9克/厘米³，用于需要很高熔体流动速率的复合基料或注塑成型场合。以下PP(聚丙烯)PP7935E1/埃克森美孚(ExxonMobil)物性表参数基本信息特性成核的刚性，高流动性高用途复合汽
-
LEXAN(沙伯基础)IR2240/PC(聚碳酸酯)物性表参数
沙伯基础SABIC塑料 LEXAN IR2240 聚碳酸酯（PC） 是 一种 中低流动性（MFR = 12,300℃/ 1.2kg）， 具有脱模功能, 符合FDA食品接触标准, 提供有限的透明色调，有限的包装类型，并且必须满足最低
-
LEONA(尼胺龙)13G43(旭化成)PA66(尼龙66)物性表参数
日本旭化成Leona PA66 13G43 是一款玻璃纤维含量为43%标准等级尼龙树脂，典型的特性是高刚性; 高强度; 良好的抗蠕变性; 耐疲劳性能，可以应用于电气/电子应用领域; 构件; 汽车的发动机罩
-
PP(聚丙烯)HF5150H|LUPOL(LG化学)物性表参数
LG化学的Lupol PP HF5150H 是一款加15%矿物填料，高流动级别的复合聚丙烯，熔融体积流量是100cm/10min，根据物理特性和加工方法其种类也多种多样，是具有代表性通用塑料中的一种，抗
-
PA6(尼龙6)BKV130H2.0/德国朗盛/物性表参数
德国朗盛 LANXESS Durethan PA6 BKV130H2.0 是一种加30%玻璃纤维，注塑，提高冲击强度，热老化稳定6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂
-
POM(聚甲醛树脂)M25S/日本宝理/物性表参数
日本宝理夺钢DURACON POM M25S 是一种标准全球品级型号,高粘度聚甲醛,夺钢就是这种共聚物的典型代表；主要以在齿轮、螺丝及轴承等机械零件方面的应用为中心。应用在DVD播放器、Blu-r
-
PA9T(尼龙9T)N1006D-H31|可乐丽(Kuraray)物性表参数
可乐丽(Kuraray)PA9T N1006D-H31是一种黑色挤出尼龙9T材料，收缩率垂直流动方向1.7%， 密度是1.06g/cm³，拉伸应力是50MPa，玻璃转化温度125°C，耐化学性良好、耐热性高,用途:管件、汽车领域的应用。PA9T(尼龙9T)N1006D-H31/可乐丽/物性表参数PDF文档下载以下是PA9T(尼龙9T)N1006D-H31|可乐丽(Kuraray)物性
-
PC(聚碳酸酯)LN-2250Y|嘉兴帝人|物性表参数
嘉兴帝人Panlite PC LN-2250Y是一款熔融体积流量是11MVR，特性是低粘度,脱模性能良好,阻燃级，应用电气元件，密度是1.20g/cm³，溶化体积流率（MVR） (300°C/1.2 kg)是11cm³/10min。嘉兴帝人Panlite PC LN-2250Y物性表参数PDF文档下载以下是PC(聚碳酸酯)LN-2250Y|嘉兴帝人|物性表参数机械性能额定值单位制测试方法拉伸模量
-
PC(聚碳酸酯)MR156/万华化学/物性表参数
万华化学Clarnate PC MR156是一种聚碳酸酯无色透明，医疗级PC，耐γ射线、电子束消毒，高粘度，易脱模，粒料，注塑，流动溶指是16,广泛用于外壳（手提机器、家电、电子机器）、充电池外壳、托盘（低温仓库）、室外安装机器外壳等。以下是PC(聚碳酸酯)MR156/万华化学/物性表参数产品特性易脱模医疗级电子束灭菌耐伽马射线中粘
-
PA6(尼龙6)C216V40|索尔维(SOLVAY)物性表参数
索尔维(SOLVAY)(原罗地亚)TECHNYL PA6 C216V40是一种加40%的玻璃纤维增强尼龙6(PA6)树脂，热稳定性能良好，用于注射成型，该产品提供了热和机械性能之间的良好结合。以下是PA6(尼龙6)C216V40|索尔维(SOLVAY)物性表参数 性能项目 试验条件[状态]&n