PA6(尼龙6)BM40XH2.0/德国朗盛/物性表参数

日期：2020-04-14 10:13:11 编辑：科思德塑胶来源：科思德塑胶浏览：256

德国朗盛LANXESS Durethan PA6 BM40XH2.0是一种加入40%矿物填充，注塑，改善流动性，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同,这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BM40XH2.0

以下是PA6(尼龙6)BM40XH2.0/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.51
	Molding shrinkage, transverse	60x60x2; 290 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.67
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.17
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.15
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	8000	4000
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	115	60
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.6
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	45	90
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	40	40
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10	<10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	40	70
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	35	35
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	8000
	Flexural strength	2 mm/min	MPa	ISO 178-A	190
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.4
	Puncture maximum force	23 °C	N	ISO 6603-2	568
	Puncture maximum force	-30 °C	N	ISO 6603-2	602
	Puncture energy	23 °C	J	ISO 6603-2	1.4
	Puncture energy	-30 °C	J	ISO 6603-2	1.5
	Ball indentation hardness		N/mm²	ISO 2039-1	213
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	220
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	191
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	215
	Temperature of deflection under load	8.00 MPa	°C	ISO 75-1,-2	80
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	215
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.35
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.85
	Burning behavior US-FMVSS302			ISO 3795	passed
Electrical properties (23 °C/50 % r. h.)
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	425
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	6
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.8
	Density		kg/m³	ISO 1183	1480
	Bulk density		kg/m³	ISO 60	900
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	290
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	280-300
	Mold temperature		°C	-	80-120

温馨提示：
本物性表参数提供者不承担任何法律责任，建议在选择材料前，就数据值与塑胶材料厂商进行验证。版权归原作者所有，如有侵权请立即与我们联系.