PA6(尼龙6)BKV25F30/德国朗盛/物性表参数

日期：2020-04-14 09:37:41 编辑：科思德塑胶来源：科思德塑胶浏览：359

德国朗盛LANXESS Durethan PA6 BKV25F30是一种加入25%玻璃纤维，注塑，阻燃，热老化稳定尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
PA6 BKV25F30

以下是PA6(尼龙6)BKV25F30/德国朗盛/物性表参数

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.3
	Molding shrinkage, transverse	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	11000	7300
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	150	90
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.3	4.4
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	55	55
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	45	50
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	10	15
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	50	55
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	45	50
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	10	15
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	10000	7000
	Flexural strength	2 mm/min	MPa	ISO 178-A	230	155
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	2.5	4.0
	Puncture maximum force	23 °C	N	ISO 6603-2	1000
	Puncture maximum force	-30 °C	N	ISO 6603-2	900
	Puncture energy	23 °C	J	ISO 6603-2	3.0
	Puncture energy	-30 °C	J	ISO 6603-2	1.9
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	205
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	215
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	205
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.4 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V	1.5 mm	Class	UL 94	5VA
	Burning behavior UL 94-5V	1.0 mm	Class	UL 94	5VA
	Burning behavior UL 94-5V	3.0 mm	Class	UL 94	5VA
	Glow wire test (GWFI)	0.4 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.4 mm	°C	IEC 60695-2-13	850
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	850
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	850
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	850
	Burning behavior US-FMVSS302			ISO 3795	passed
Electrical properties (23 °C/50 % r. h.)
	Volume resistivity		Ohm·m	IEC 60093	3.4E12
	Surface resistivity		Ohm	IEC 60093	4.1E13
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	400
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	4.3
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.3
	Density		kg/m³	ISO 1183	1600
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-100