PA6(尼龙6)BG60XXF/德国朗盛/物性表参数

日期：2020-04-25 02:35:45 编辑：科思德塑胶来源：科思德塑胶浏览：287

德国朗盛LANXESS Durethan PA6 BG60XXF是一种加60%玻璃纤维，注塑成型，热老化稳定，提高流动性，低翘曲倾向尼龙6树脂，尼龙从环境中吸收潮气的能力也不同。这与增塑剂的效果相同，即可以提高材料的断裂伸长及韧性，但降低了材料的強度和剛度,除了自然色及黑色外，还可以提供一系列的不透明标准颜色；如有需要，也可以提供特定颜色的产品。
生产商：LANXESS(德国朗盛)、品名：Durethan
PA6(尼龙6)BG60XXF/德国朗盛/物性表参数

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 270 °C / WZ 80 °C; 500 bar	%	acc. ISO 2577	0.2
	Molding shrinkage, transverse	150x105x3; 270 °C / WZ 80 °C; 500 bar	%	acc. ISO 2577	0.55
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.05
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.1
	Molding shrinkage, parallel	60x60x2; 270 °C / WZ 120 °C; 600 bar	%	ISO 294-4	0.35
	Molding shrinkage, transverse	60x60x2; 270 °C / WZ 120 °C; 600 bar	%	ISO 294-4	0.4
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.05
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.05
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	19000	12300
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	210	135
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.2	3.3
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	85	75
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	75	70
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	15	20
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	15	15
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	80	70
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	75	65
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	15	20
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	15	15
	Flexural modulus	2 mm/min	MPa	ISO 178-A	18000	12000
	Flexural strength	2 mm/min	MPa	ISO 178-A	340	210
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	2.5	3
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	221
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	210
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	218
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.11
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.85
Other properties (23 °C)
	Density		kg/m³	ISO 1183	1680
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	270
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.05-0.15
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120